میگنیشیا آئرن اسپنل برک

Magnesia iron spinel brick is an excellent product of a “chrome-free” سیمنٹ بھٹہ فائرنگ زون. اس میں بھٹے کی جلد کو لٹکانے کی بہترین صلاحیت ہے۔, اچھا تھرمل جھٹکا استحکام, cement clinker erosion resistance, and a low thermal expansion rate. It has an excellent application effect in cement kiln firing zones.

Magnesia iron spinel brick ingredients

Magnesia-iron-spinel bricks use high-purity magnesia and aluminum-iron spinel as the main raw materials and are formed through proportioning and high pressure. The firing temperature and time must be strictly controlled during the production process.

میگنیشیا آئرن اسپنل اینٹوں کے پیرامیٹرز

آئٹم	انڈیکس
	Magnesia iron Spinel Brick	High toughness Magnesium Iron Spinel brick
MgO %	≥85	≥88
فے2اے3  %	5~7.5	5~6
ال2اے3  %	3~5	4~7
Bulk density g/cm3	≥3	≥2.9
Apparent porosity %	≤17	≤16
Cold Crushing Strength MPa	≥45	≥55
Thermal shock resistance cycle 1100℃water cooling	≥6	≥8
0.2MPa Refractoriness under load ℃	≥1600	≥1650
Thermal expansion rate % 1400℃	≤1.6	≤1.7
Thermal conductivity W/(m·K)  350±25℃	≤2.6	≤2.6

The production process of magnesia iron spinel brick

Batching → mold installation → raw material mixing → vibration forming → de-molding → drying at 200°C → calcination at 350°C → packaging → storage

رونگشینگ میگنیشیا آئرن اسپنل اینٹوں کے معیار کو کیسے کنٹرول کرتا ہے؟

مواد کو سختی سے منتخب کریں۔

اعلی معیار کی پیداوار کا خام مال منتخب کریں اور پیشہ ورانہ اقدامات کے مطابق پیداوار کریں۔.

پیشہ ور ٹیم

کمپنی کے پاس پیشہ ور تکنیکی پروڈکشن ٹیم اور پروڈکشن کا سامان ہے۔.

حسب ضرورت پروسیسنگ

To meet the production needs of customers, فیکٹری حسب ضرورت کی حمایت کرتی ہے اور کسٹمر ڈرائنگ کے مطابق پیدا کرسکتی ہے۔.