Chrome corundum has excellent properties and is widely used in high-temperature fields with harsh environments, including non-ferrous metallurgical kilns, glass melting furnaces, carbon black reactors, waste incinerators, vesaire.

Krom içeren refrakter malzemeler, benzersiz özelliklerinden dolayı demir dışı metalurji fırınlarında iyi etkilere sahiptir.. Her ne kadar birçok bilim adamı demir dışı metalurjide kullanılan krom içermeyen refrakter malzemeleri inceliyor olsa da, the use of chromium-containing refractory materials as smelting furnace linings in non-ferrous metallurgy is still the mainstream. Ek olarak, chromium-containing refractory materials are also used in zinc volatilization kilns, copper converters, coal gasification furnaces, and carbon black reactors.

Aluminum-chromium refractory materials as lining materials

Aluminum-chromium refractory materials are also commonly used in carbon black reactors, including the combustion section, throat section, reaction section, vesaire. Aluminum-chromium refractory materials serve in the ultra-high temperature (19009℃) area of ​​carbon black reactors, chemical erosion areas of reducing gases (C, CO, H2) and ash, and areas with frequent temperature fluctuations.

Öyleyse, the aluminum-chromium refractory materials used in carbon black reactors should have the following characteristics:

1. Yüksek refrakterlik, yüksek yük yumuşatma sıcaklığı, and low high-temperature thixotropy rate;
2. Stability under a strong reducing atmosphere;
3. Strong resistance to molten ash erosion;
4. High high temperature strength and anti-scouring performance;
5. İyi termal şok direnci

Among the ısıya dayanıklı malzemeler used for the lining of the garbage melting incinerator (ash melting furnace), the refractory materials containing gasified tantalum generally show good corrosion resistance. When the combustion temperature is higher than 1250℃, chrome corundum products are used. The garbage melting incinerator is generally an oxidizing atmosphere, so C-5iC bricks and SiC bricks with poor oxidation resistance cannot be used, and A1203-Cr203 materials and Mg0-Cr203 materials are preferably used. Genel olarak, the erosion rate of AI203-Cr203 materials increases with the increase of basicity, so it is mainly used in melting furnaces with relatively low basicity.