วัสดุกระแทกอลูมิเนียมซิลิเกต

Aluminum silicate ramming material is a kind of refractory material with high aluminum and low iron, and its main components are Al₂อ₃ and SiO₂. It is made by high-temperature sintering and high-energy grinding or ramming. It has high service temperature, strength, and density, and is mainly used in high-demand refractory structures. Rongsheng Refractory Materials also produces หล่อได้ and customized ramming materials with different compositions.

Aluminum silicate ramming material details

รายการ	Alumina-Silicon			Silicon- Carbide			เซอร์โคเนียม โครเมียม คอรันดัม
	KSL-1	KSL-	KSL-	KSL-	KSL-	KSL-	KSL-
อัล2O3 %	≥65	≥75	≥85	/	/	/	≥80
ซิซี %	/	/	/	≥40	≥60	≥70	/
Cr2O3 %	/	/	/	/	/	/	≥3
ZrO2 %	/	/	/	/	/	/	≥2
Bulk Density g/cm3 110℃×24h	≥2.5	≥2.7	≥2.8	≥2.4	≥2.5	≥2.6	≥2.8
Permanent Linear Change Rate % 1000℃×3h	-0.4~0	-0.5~0	-0.5~0	-0.4~0	-0.5~0	-0.6~0	-0.6~0
Cold Crushing strength MPa 1000℃×3ชม	≥70	≥80	≥90	≥60	≥70	≥80	≥90
Wear resistance at room temperature cm3 1000℃×3h	≤7	≤6	≤5	≤7	≤6	≤5	≤5
Thermal shock resistance 1000℃ water cooling cycle 1000℃×3h Fired	≥30	≥30	≥25	≥30	≥35	≥40	≥30
Plasticity Index %	15~55
Thermal conductivity W/(เอ็ม·เค) 1000℃	1.1~1.6		1.6~2.0	3~5	5~7	6~8	2~3

Production of aluminum silicate ramming mass

In manufacturing, aluminum silicate ramming materials usually need to go through multiple processes, such as screening, การอบแห้ง, mixing, pounding, เป็นต้น, to ensure uniformity and stability. Its production process and formula can be adjusted according to different needs to achieve the required fire resistance and service life.

Features of aluminum silicate ramming mass

1. High aluminum and low iron: อัล₂อ₃ content is usually 55-80%, and Fe₂อ₃ content is shallow, generally not more than 3%. This can greatly increase the softening point and use temperature.
2. Dense structure: Aluminum silicate ramming material has been rammed to obtain magnificent grain structure and higher density, generally greater than 3.4g/cm³, which greatly improves its strength and slag erosion resistance.
3. High corrosion resistance: The composition of high aluminum and low iron and dense microstructure make aluminum silicate ramming material have strong resistance to acid and alkali and corrosion of various slags.
4. มีความแข็งแรงสูง: the compressive strength of aluminum silicate ramming material exceeds 600MPa, which enables it to withstand greater mechanical stress and service load.
5. High working temperature: โดยทั่วไป, it can work at a temperature above 1600-1800°C, and the maximum temperature of special varieties can reach above 2000°C.
   

1. ถาม:คุณจะควบคุมคุณภาพของคุณได้อย่างไร? ก：ระหว่างกระบวนการผลิต, เรามีระบบควบคุมคุณภาพองค์ประกอบทางเคมีที่สมบูรณ์. หลังจากการผลิต, สินค้าทั้งหมดจะได้รับการทดสอบ, และจะมีการออกใบรับรองคุณภาพให้กับสินค้า. 2. ถาม:เวลาจัดส่งของคุณคืออะไร? ก：ขึ้นอยู่กับปริมาณสินค้าที่ซื้อ, เวลาทั่วไปคือ 7-12 วัน. หากเป็นสินค้าสั่งทำพิเศษ, อาจใช้เวลานานกว่านี้. 3. ถาม:คุณให้ตัวอย่าง? ก：ใช่, เราสามารถจัดหาตัวอย่าง 4. ถาม:เราสามารถเยี่ยมชมบริษัทของคุณ? ก：ใช่, แน่นอน. ยินดีต้อนรับสู่ประเทศจีนและเรารู้สึกเป็นเกียรติที่มีลูกค้าและเพื่อน. 5.ถาม: สามารถปรับแต่งผลิตภัณฑ์? ก：เราสนับสนุนการปรับแต่ง, คุณสามารถส่งแผนและแบบการออกแบบของคุณมาให้เรา, และเราจะจัดทำแผนการผลิตที่สมบูรณ์. 6. ถาม:มีที่มาที่ไปอย่างไร? ก：จาก เจิ้งโจว, เหอหนาน, จีน, 7.ถาม: วิธีแพ็ค ก：Aluminum silicate ramming material is bagged