Mullite insulation brick is made of high-alumina bauxite clinker as the main material, plus a small amount of clay or raw bauxite as a binder, and then shaped and sintered at high temperatures.

Mullite refractory bricks are also called lightweight mullite brick and mullite thermal insulation brick, Mullite insulation brick is a high-alumina refractory material with mullite (3Al₂O₃·2SiO₂) as the main crystal phase. Generally, the alumina content is between 40% and 75%. Those with lower aluminum content also contain a small amount of glass phase and cristobalite, and those with higher alumina content also contain a small amount of corundum.

refractory brick

Mullite insulation brick parameters

Physical and chemical indicators：

Item		Index
Item		JM23	JM25	JM26	JM27
Al₂O₃ %		≥40	≥50	≥55	≥60
Fe₂O₃ %		≤1.0	≤1.0	≤0.9	≤0.8
Apparent porosity %		≤0.55	≤0.80	≤0.85	≤0.9
Cold Crush Strength MPa		≥1.0	≥1.5	≥2.0	≥2.5
Permanent Linear Change Rate %		1230℃×12h	1350℃×12h	1400℃×12h	1450℃×12h
Permanent Linear Change Rate %		-1.5~0.5
Thermal Conductivity W/(m·K)	200±25℃	≤0.18	≤0.26	≤0.28	≤0.32
	350±25℃	≤0.20	≤0.28	≤0.30	≤0.32
	600±25℃	≤0.22	≤0.30	≤0.33	≤0.36
0.05MPa Refractoriness Under LoadT_0.5 ℃		≥1080	≥1200	≥1250	≥1300

Item		Index
Item		JM28	JM30	JM32
Al₂O₃ %		≥65	≥70	≥77
Fe₂O₃ %		≤0.7	≤0.6	≤0.5
Apparent porosity %		≤0.95	≤1.05	≤1.35
Cold Crush Strength MPa		≥2.5	≥3.0	≥3.5
Permanent Linear Change Rate %		1510℃×12h	1620℃×12h	1730℃×12h
Permanent Linear Change Rate %		-1.5~0.5
Thermal Conductivity W/(m·K)	200±25℃	≤0.35	≤0.42	≤0.56
	350±25℃	≤0.37	≤0.44	≤0.60
	600±25℃	≤0.39	≤0.46	≤0.64
0.05MPa Refractoriness Under Load T_0.5 ℃		≥1360	≥1470	≥1570

refractory mullite brick

Mullite insulation brick advantages

Low heat fusion
Low thermal conductivity
High refractoriness
Good chemical stability
High compressive and flexural strength
Accurate appearance and size

Mullite insulating brick application

Mullite insulating bricks are suitable for lining cracking furnaces, hot blast furnaces, ceramic roller kilns, electric porcelain drawer kilns, glass crucibles, and various electric furnaces. It is used for the roof of the hot blast stove, furnace body and bottom of blast furnaces, regenerator of glass melting furnaces, ceramic sintering kiln, furnace lining of petroleum cracking system, ва ғайра. Mullite insulation bricks also have the characteristics of high load softening temperature, compact structure, low porosity, and good erosion resistance.

Mullite insulation brick refractories company

Insulating fire bricks success case

The refractory bricks of Rongsheng Refractories Co., Ltd. have been sold to more than 80 countries, including Russia, Uzbekistan, Ecuador, Chile, South Africa, Portugal, and other places. Customers are very satisfied with this mullite JM brick.

FAQ of mullite refractory bricks

What is the operating temperature range of mullite refractory bricks?

The operating temperature range of mullite insulation bricks is generally 1000°C-1650°C, and can be customized according to specific use requirements.

Can the size and shape be customized?

Yes, Support customization.

What are the precautions for storage and transportation?

Store in a dry and ventilated warehouse to avoid moisture. During transportation, care should be taken to avoid severe vibration and collision to avoid damage.

Contact us

About Rongsheng Group

Rongsheng is a refractory exporter with 10 таҷрибаи солонаи содирот. We have rich experience in refractory products and can provide customers with a complete set of kiln refractory usage solutions. Mullite insulation bricks are very popular refractory materials, and high alumina bricks, хишти корунд and хишти карбон магнезия are also popular products.

$mullite refractory bricks shipping$

mullite refractory bricks shipping

The production time and transportation time are generally about 7-12 days, but this is related to the quantity ordered, but it will definitely be delivered according to the time stipulated in the contract. For details, please contact us.