Material de batere silicat de aluminiu

Aluminum silicate ramming material is a kind of refractory material with high aluminum and low iron, and its main components are Al₂O₃ and SiO₂. It is made by high-temperature sintering and high-energy grinding or ramming. It has high service temperature, strength, and density, and is mainly used in high-demand refractory structures. Rongsheng Refractory Materials also produces castables and customized ramming materials with different compositions.

Aluminum silicate ramming material details

Articol	Alumina-Silicon			Silicon- Carbide			Zirconium Chrome Corundum
	KSL-1	KSL-	KSL-	KSL-	KSL-	KSL-	KSL-
Al2O3 %	≥65	≥75	≥85	/	/	/	≥80
Sic %	/	/	/	≥40	≥60	≥70	/
Cr2O3 %	/	/	/	/	/	/	≥3
ZrO2 %	/	/	/	/	/	/	≥2
Bulk Density g/cm3 110℃×24h	≥2,5	≥2.7	≥2.8	≥2.4	≥2,5	≥2.6	≥2.8
Permanent Linear Change Rate % 1000℃×3h	-0.4~0	-0.5~0	-0.5~0	-0.4~0	-0.5~0	-0.6~0	-0.6~0
Cold Crushing strength MPa 1000℃×3h	≥70	≥80	≥90	≥60	≥70	≥80	≥90
Wear resistance at room temperature cm3 1000℃×3h	≤7	≤6	≤5	≤7	≤6	≤5	≤5
Thermal shock resistance 1000℃ water cooling cycle 1000℃×3h Fired	≥30	≥30	≥25	≥30	≥35	≥40	≥30
Plasticity Index %	15~55
Thermal conductivity W/(m·K) 1000℃	1.1~1.6		1.6~2.0	3~5	5~7	6~8	2~3

Production of aluminum silicate ramming mass

In manufacturing, aluminum silicate ramming materials usually need to go through multiple processes, such as screening, uscare, amestecarea, pounding, etc., to ensure uniformity and stability. Its production process and formula can be adjusted according to different needs to achieve the required fire resistance and service life.

Features of aluminum silicate ramming mass

1. High aluminum and low iron: Al₂O₃ content is usually 55-80%, and Fe₂O₃ content is shallow, generally not more than 3%. This can greatly increase the softening point and use temperature.
2. Dense structure: Aluminum silicate ramming material has been rammed to obtain magnificent grain structure and higher density, generally greater than 3.4g/cm³, which greatly improves its strength and slag erosion resistance.
3. High corrosion resistance: The composition of high aluminum and low iron and dense microstructure make aluminum silicate ramming material have strong resistance to acid and alkali and corrosion of various slags.
4. Putere mare: the compressive strength of aluminum silicate ramming material exceeds 600MPa, which enables it to withstand greater mechanical stress and service load.
5. High working temperature: În general, it can work at a temperature above 1600-1800°C, and the maximum temperature of special varieties can reach above 2000°C.
   

1. Q:Cum vă controlați calitatea? A：În timpul procesului de producție, avem un sistem complet de control al calității compoziției chimice. După producție, toate bunurile vor fi testate, iar cu marfa se va elibera un certificat de calitate. 2. Q:Care este timpul dvs. de livrare? A：In functie de cantitatea de produse achizitionate, timpul general este 7-12 zile. Daca este un produs personalizat, poate dura mai mult. 3. Q:Oferiți mostre? A：da, putem oferi mostre 4. Q:Putem vizita compania dvs? A：da, desigur. Sunteți foarte bineveniți în China și vom fi onorați să avem un client și un prieten. 5.Q: Produsul poate fi personalizat? A：Suportăm personalizarea, ne puteți trimite planul și desenul dvs. de design, și vom face un plan complet de producție. 6. Q:Unde este locul de origine? A：Din Zhengzhou, Henan, China, 7.Q: Cum să împachetezi A：Aluminum silicate ramming material is bagged