Wat zijn de vuurvaste materialen voor cementdraaiovens??

Cementdraaiovens zijn een essentieel onderdeel van het cementproductieproces. Het vereist vuurvaste materialen die bestand zijn tegen hoge temperaturen en chemische aanvallen. Wat zijn de vuurvaste materialen voor cementdraaiovens??

Magnesium-iron aluminum spinel brick

Magnesia-iron-aluminum spinel bricks are made of high-purity magnesia and iron-aluminum spinel as raw materials; through reasonable proportioning, hogedrukgieten, and strict control of firing temperature and firing atmosphere, magnesia-iron-aluminum spinel bricks have good flexibility It has good thermal shock stability, high-temperature volume stability, high load-softening temperature, and excellent kiln-hanging performance.

Magnesia calcium brick

Magnesia-calcium brick is an alkaline refractory material made of condensed magnesia-calcium sand. Usually, the CaO content reaches more than 40%. It is mainly used in the firing zone of rotary kilns.

Magnesium zirconium brick

It uses fused magnesia and zircon sand as the primary raw materials and is produced by high-pressure molding and high-temperature firing. It has a dense structure, small and evenly distributed pores, sterkte bij hoge temperaturen, goede thermische schokstabiliteit, excellent alkali erosion resistance, and excellent kiln-hanging performance. It is suitable for the firing zone of cement rotary kilns.

Magnesia-aluminum spinel brick

It uses high-purity magnesia and synthetic magnesia-aluminum spinel brick as the main raw materials. The main crystal phases are periclase and spinel. It has good corrosion resistance, afbrokkelende weerstand, and high-temperature resistance. It can be used in the transition zone of large dry cement rotary kilns.

Silica mullite bricks

It is made of special-grade high-aluminum clay material, silicium carbide, and metallic silicon as the main raw materials, through high-pressure molding and high-temperature firing. It has high strength at normal and high temperatures, goede thermische schokstabiliteit, continuously forms a protective layer during use, and has good wear resistance and strong spalling resistance. It is suitable for the lower transition zone, cooling zone, kiln mouth, and other parts of cement kilns.

Anti-flaking hoge aluminiumoxide bakstenen

Using special-grade high-alumina clinker as the main raw material, the thermal shock stability is improved by adding phase change raw materials such as diamond sand, kyanite, and alusite. It has strong resistance to spalling, corrosion resistance to potassium, natrium, sulfur, chlorine, and alkaline salts, and low thermal conductivity. It is an ideal material for the transition zone and decomposition zone of cement kilns. It can also be used for kiln door covers and cooling of cement kilns and other parts.

Alkali-resistant bricks

Alkali-resistant bricks: Alkali-resistant brick products have the characteristics of stable volume, strong resistance to alkali erosion, and resistance to penetration. They are used in preheaters, decomposition furnaces, tertiary air ducts, and other parts of cement kilns.

Alkali-resistant castable

Alkali-resistant castables: Alkali-resistant castables are made of aluminum silicate materials as refractory aggregates and powders, and aluminate cement and admixtures. It has good high-temperature performance and alkali corrosion resistance. The high-strength type also has high strength and good wear resistance. It can be used in systems such as preheaters and air ducts of large and medium-sized dry process cement kilns.

Steel fiber reinforced refractory castable

Steel fiber reinforced refractory castable: Using high alumina phosphate clinker or corundum as aggregate and powder, adding binding agent and the appropriate amount of heat-resistant stainless steel fiber, it has high strength, goede taaiheid, goede thermische schokstabiliteit, resistance to spalling, and Features of strong wear resistance. Used in cement rotary kiln mouth, cooler, decomposition furnace, preheater, en andere onderdelen.