Magnesia Alumina Spinelsteen

Magnesia-alumina spinel brick is made of magnesia-alumina spinel ((MgAl₂O₄ abbreviated as MA)) as the matrix, using high-quality high-purity magnesia and Al₂O₃-containing ore, through batching, mengen, billet making, drogen, firing and other processes. Alkaline refractory products are known for their superior thermal shock resistance to magnesia bricks and are widely used in masonry cement rotary kilns, lime rotary kilns, open hearth furnaces, elektrische oven daken, enz.

Magnesium aluminum spinel brick parameters

Item	Inhoudsopgave
	MLJ-90	MLJ-85	MLJ-80	MLJ-75
MgO %	≥90	≥85	≥80	≥75
Al2O3  %	3~8	5~12	8~17	≥8~12
Schijnbare porositeit %	≤17	≤17	≤16	≤19
Bulkdichtheid g/cm3	≥2,95	≥2,95	≥2.90	≥2.85
Koude breeksterkte MPa	≥45	≥45	≥55	≥40
0.2MPa Vuurvastheid onder belasting ℃	≥1700			≥1650
Thermische schokbestendigheidscyclus 1100 ℃ waterkoeling	≥3	≥8	≥12	≥8

Magnesia alumina spinel bricks application

Magnesia-aluminum spinel bricks are often used in the transition zone of the rotary kiln, the kiln mouth, the inner lining of the cooler, and other important parts.

Rongsheng bedrijf introductie

Rongsheng Company is a professional supplier of refractory materials, met 10 jaar exportervaring, exporteren naar meer dan 80 landen. De belangrijkste producten van Rongsheng Company omvatten verschillende vuurvaste stenen, ongevormde vuurvaste materialen, metallurgische materialen, thermische isolatiematerialen enzovoort.

onze service

1. Ondersteuning fabrieksbezoek
2. Ondersteuning van productaanpassing
3. Goede service na verkoop
4. Aangewezen vuurvaste oplossingen
5. Monsters kunnen worden verstrekt

Vraag een offerte aan