JM23 JM26 JM28 JM30 Mullite Tiwhi Pereki

Mullite insulation brick is made of high-alumina bauxite clinker as the main material, plus a small amount of clay or raw bauxite as a binder, and then shaped and sintered at high temperatures.

Mullite refractory bricks are also called lightweight mullite brick and mullite thermal insulation brick, Mullite insulation brick is a high-alumina refractory material with mullite (3Ko Al₂O₃·2SiO₂) as the main crystal phase. Generally, the alumina content is between 40% a 75%. Those with lower aluminum content also contain a small amount of glass phase and cristobalite, and those with higher alumina content also contain a small amount of corundum.

Mullite insulation brick parameters

Physical and chemical indicators：

Tūemi		Taurangi
		JM23	JM25	JM26	JM27
Ko Al2O3  %		≥40	≥50	≥55	≥60
Fe2O3  %		≤1.0	≤1.0	≤0.9	≤0.8
Te porosity %		≤0.55	≤0.80	≤0.85	≤0.9
Cold Crush Strength MPa		≥1.0	≥1.5	≥2.0	≥2.5
Permanent Linear Change Rate %		1230℃×12h	1350℃×12h	1400℃×12h	1450℃×12h
		-1.5~0.5
Thermal Conductivity W/(m·K)	200±25℃	≤0.18	≤0.26	≤0.28	≤0.32
	350±25℃	≤0.20	≤0.28	≤0.30	≤0.32
	600±25℃	≤0.22	≤0.30	≤0.33	≤0.36
0.05MPa Refractoriness Under LoadT0.5 ℃		≥1080	≥1200	≥1250	≥1300

Tūemi		Taurangi
		JM28	JM30	JM32
Ko Al2O3  %		≥65	≥70	≥77
Fe2O3  %		≤0.7	≤0.6	≤0.5
Te porosity %		≤0.95	≤1.05	≤1.35
Cold Crush Strength MPa		≥2.5	≥3.0	≥3.5
Permanent Linear Change Rate %		1510℃×12h	1620℃×12h	1730℃×12h
		-1.5~0.5
Thermal Conductivity W/(m·K)	200±25℃	≤0.35	≤0.42	≤0.56
	350±25℃	≤0.37	≤0.44	≤0.60
	600±25℃	≤0.39	≤0.46	≤0.64
0.05MPa Refractoriness Under Load T0.5 ℃		≥1360	≥1470	≥1570

Mullite insulation brick advantages

1. Low heat fusion
2. Low thermal conductivity
3. High refractoriness
4. Good chemical stability
5. High compressive and flexural strength
6. Accurate appearance and size

Mullite insulating brick application

Mullite insulating bricks are suitable for lining cracking furnaces, hot blast furnaces, ceramic roller kilns, electric porcelain drawer kilns, glass crucibles, and various electric furnaces. It is used for the roof of the hot blast stove, furnace body and bottom of blast furnaces, regenerator of glass melting furnaces, ceramic sintering kiln, furnace lining of petroleum cracking system, etc. Mullite insulation bricks also have the characteristics of high load softening temperature, compact structure, porosity iti, and good erosion resistance.

Mullite insulation brick refractories company

Insulating fire bricks success case

The refractory bricks of Rongsheng Refractories Co., Ltd. have been sold to more than 80 whenua, including Russia, Uzbekistan, Ecuador, Chile, South Africa, Portugal, and other places. Customers are very satisfied with this mullite JM brick.

FAQ of mullite refractory bricks

Contact us

Rongsheng is a refractory exporter with 10 tau o te wheako kaweake. We have rich experience in refractory products and can provide customers with a complete set of kiln refractory usage solutions. Mullite insulation bricks are very popular refractory materials, a high alumina bricks, pereki corundum a pereki waro magnesia are also popular products.

 

The production time and transportation time are generally about 7-12 days, but this is related to the quantity ordered, but it will definitely be delivered according to the time stipulated in the contract. For details, tēnā whakapā mai.