시멘트 회전 가마의 내화물은 무엇입니까?

Cement rotary kilns are an essential piece of equipment in the cement production process. It requires refractory materials to resist high temperatures and chemical attacks. 시멘트 회전 가마의 내화물은 무엇입니까?

Magnesium-iron aluminum spinel brick

Magnesia-iron-aluminum spinel bricks are made of high-purity magnesia and iron-aluminum spinel as raw materials; through reasonable proportioning, 고압 성형, and strict control of firing temperature and firing atmosphere, magnesia-iron-aluminum spinel bricks have good flexibility It has good thermal shock stability, high-temperature volume stability, high load-softening temperature, and excellent kiln-hanging performance.

Magnesia calcium brick

Magnesia-calcium brick is an alkaline refractory material made of condensed magnesia-calcium sand. 대개, the CaO content reaches more than 40%. It is mainly used in the firing zone of rotary kilns.

Magnesium zirconium brick

It uses fused magnesia and zircon sand as the primary raw materials and is produced by high-pressure molding and high-temperature firing. It has a dense structure, small and evenly distributed pores, 고온 강도, 좋은 열충격 안정성, excellent alkali erosion resistance, and excellent kiln-hanging performance. It is suitable for the firing zone of cement rotary kilns.

Magnesia-aluminum spinel brick

It uses high-purity magnesia and synthetic magnesia-aluminum spinel brick as the main raw materials. The main crystal phases are periclase and spinel. It has good corrosion resistance, spalling resistance, and high-temperature resistance. It can be used in the transition zone of large dry cement rotary kilns.

Silica mullite bricks

It is made of special-grade high-aluminum clay material, 탄화규소, and metallic silicon as the main raw materials, through high-pressure molding and high-temperature firing. It has high strength at normal and high temperatures, 좋은 열충격 안정성, continuously forms a protective layer during use, and has good wear resistance and strong spalling resistance. It is suitable for the lower transition zone, 냉각 구역, kiln mouth, and other parts of cement kilns.

Anti-flaking 높은 알루미나 벽돌

Using special-grade high-alumina clinker as the main raw material, the thermal shock stability is improved by adding phase change raw materials such as diamond sand, kyanite, and alusite. It has strong resistance to spalling, corrosion resistance to potassium, 나트륨, 황, chlorine, and alkaline salts, 열전도율이 낮고. It is an ideal material for the transition zone and decomposition zone of cement kilns. It can also be used for kiln door covers and cooling of cement kilns and other parts.

내알칼리성 벽돌

내알칼리성 벽돌: Alkali-resistant brick products have the characteristics of stable volume, strong resistance to alkali erosion, and resistance to penetration. They are used in preheaters, decomposition furnaces, tertiary air ducts, and other parts of cement kilns.

Alkali-resistant castable

Alkali-resistant castables: Alkali-resistant castables are made of aluminum silicate materials as refractory aggregates and powders, and aluminate cement and admixtures. It has good high-temperature performance and alkali corrosion resistance. The high-strength type also has high strength and good wear resistance. It can be used in systems such as preheaters and air ducts of large and medium-sized dry process cement kilns.

강철 섬유 강화 내화물 캐스터블

강철 섬유 강화 내화물 캐스터블: Using high alumina phosphate clinker or corundum as aggregate and powder, adding binding agent and the appropriate amount of heat-resistant stainless steel fiber, 그것은 강도가 높다, 좋은 인성, 좋은 열충격 안정성, resistance to spalling, and Features of strong wear resistance. Used in cement rotary kiln mouth, cooler, decomposition furnace, preheater, 및 기타 부품.