What are the refractory materials for cement rotary kilns?

Cement rotary kilns are an essential piece of equipment in the cement production process. It requires refractory materials to resist high temperatures and chemical attacks. What are the refractory materials for cement rotary kilns?

Magnesium-iron aluminum spinel brick

Magnesia-iron-aluminum spinel bricks are made of high-purity magnesia and iron-aluminum spinel as raw materials; through reasonable proportioning, high-pressure molding, and strict control of firing temperature and firing atmosphere, magnesia-iron-aluminum spinel bricks have good flexibility It has good thermal shock stability, high-temperature volume stability, high load-softening temperature, and excellent kiln-hanging performance.

Magnesia calcium brick

Magnesia-calcium brick is an alkaline refractory material made of condensed magnesia-calcium sand. いつもの, the CaO content reaches more than 40%. It is mainly used in the firing zone of rotary kilns.

Magnesium zirconium brick

It uses fused magnesia and zircon sand as the primary raw materials and is produced by high-pressure molding and high-temperature firing. It has a dense structure, small and evenly distributed pores, high-temperature strength, 良好な熱衝撃安定性, excellent alkali erosion resistance, and excellent kiln-hanging performance. It is suitable for the firing zone of cement rotary kilns.

Magnesia-aluminum spinel brick

It uses high-purity magnesia and synthetic magnesia-aluminum spinel brick as the main raw materials. The main crystal phases are periclase and spinel. It has good corrosion resistance, 耐剥離性, and high-temperature resistance. It can be used in the transition zone of large dry cement rotary kilns.

Silica mullite bricks

It is made of special-grade high-aluminum clay material, 炭化ケイ素, and metallic silicon as the main raw materials, through high-pressure molding and high-temperature firing. It has high strength at normal and high temperatures, 良好な熱衝撃安定性, continuously forms a protective layer during use, and has good wear resistance and strong spalling resistance. It is suitable for the lower transition zone, 冷却ゾーン, kiln mouth, and other parts of cement kilns.

Anti-flaking 高アルミナレンガ

Using special-grade high-alumina clinker as the main raw material, the thermal shock stability is improved by adding phase change raw materials such as diamond sand, kyanite, and alusite. It has strong resistance to spalling, corrosion resistance to potassium, ナトリウム, 硫黄, chlorine, and alkaline salts, 熱伝導率が低い. It is an ideal material for the transition zone and decomposition zone of cement kilns. It can also be used for kiln door covers and cooling of cement kilns and other parts.

耐アルカリレンガ

耐アルカリレンガ: Alkali-resistant brick products have the characteristics of stable volume, strong resistance to alkali erosion, and resistance to penetration. They are used in preheaters, decomposition furnaces, tertiary air ducts, and other parts of cement kilns.

Alkali-resistant castable

Alkali-resistant castables: Alkali-resistant castables are made of aluminum silicate materials as refractory aggregates and powders, and aluminate cement and admixtures. It has good high-temperature performance and alkali corrosion resistance. The high-strength type also has high strength and good wear resistance. It can be used in systems such as preheaters and air ducts of large and medium-sized dry process cement kilns.

鋼繊維強化耐火物キャスタブル

鋼繊維強化耐火物キャスタブル: Using high alumina phosphate clinker or corundum as aggregate and powder, adding binding agent and the appropriate amount of heat-resistant stainless steel fiber, 高い強度を持っています, 良好な靭性, 良好な熱衝撃安定性, resistance to spalling, and Features of strong wear resistance. Used in cement rotary kiln mouth, cooler, decomposition furnace, preheater, and other parts.