耐火物キャスタブル are a widely used material in high temperature industrial applications, 特に製錬などの産業では, セラミックス, そしてガラス. In order to improve the performance and stability of castables, anchor fire bricks are introduced as key components.

耐火物キャスタブルの使用におけるアンカー耐火レンガの役割

アンカーレンガ play the role of skeleton in refractory castables. So anchor bricks are also called hanging bricks. There are three products that play the role of the skeleton in the use of refractory castables: one is anchor bricks, the other is anchors, and the third is tortoiseshell nets. Anchors and tortoise shell nets are both metal products, and only anchor bricks are 耐火製品.

Size and shape of anchor fire bricks

There are many shapes and connection methods for anchoring fire bricks, and their sizes are different. 一般的に, they are made according to user customization. There are also some regular lengths of 330, 380, 440, and 500m. The thickness is generally around 100mm. The function of anchoring bricks is to enhance the strength of the refractory castable lining.
Anchoring bricks are divided into those with holes and those without holes. The use of those with holes and those without holes is different from the use of furnace roofs and furnace walls. They are used to be embedded in the castable and hung with hanging parts, so they can also be called hanging bricks.

Anchor nail introduction

The anchor is directly welded on the furnace shell. When the refractory castable is poured, the anchor is buried in the lining to anchor and connect. The most commonly used ones are Y, V, and L shapes. The height is determined according to the thickness of the refractory castable. If the thickness of the castable is 200mm, the height of the anchor can be 160-180mm. The anchor is very easy to oxidize at high temperatures. When buried in the castable lining, it should be determined according to the thickness of the lining and the use temperature.

Production of anchor bricks

Anchor refractory bricks are refractory bricks that are made by mixing raw materials, 成形, and sintering. They have high strength, 良好な熱衝撃安定性, and toughness. しかし, the mold of anchor bricks is a difficult point in the production process. The mold is complex and difficult to make, and the mold cost is much higher than that of general refractory bricks.
If the anchor brick has a hole, the installation hole is generally at the neck. The finished anchor brick must not have cracks and the size must be accurate. It is convenient to use on the furnace top. Anchor bricks generally use grade 3 high aluminum more, because grade 3 high aluminum anchor bricks are tough. Although the first-grade high aluminum bricks have good quality, the hardness also increases. When used in general castables, cracks are prone to occur.