Üvegkemencében tűzálló tégla

Float glass furnace

Float glass furnace refractories for each part

1. L-shaped hanging wall

Silica brick

2. Melting part

Fused Brick Silica Brick

3. Stuck neck

Silica brick

4. Cooling unit

Corundum refractories, silica bricks

5. Annealing kiln, regenerator

High alumina bricks, agyagtéglák, directly bonded magnesia chrome bricks

Glass production process

Glass: an amorphous solid substance obtained by cooling and hardening of a molten substance. The production process includes the preparation of raw materials – the melting of molten glass – the shaping of glass products – the annealing of glass products. The process in the glass kiln includes the mixing of glass batch materials in a reasonable It melts into a liquid phase under the temperature regime, homogenizes and clarifies it, and becomes a transparent liquid.

Silica brick

Silica bricks are refractory products with a SiO2 content of more than 93%. They are made from silica with a silicon content of >96%, adding mineralizers and binders, and then mixing, shaping, szárítás, and firing. They are mainly used for coke oven carbonization. Chambers, combustion chambers and partition walls, glass kiln roofs, kiln walls, high-temperature load-bearing parts of hot blast furnaces carbon roasting furnaces, and other kilns. True density <2.35. It is an acidic refractory material, which is highly resistant to acidic slag or acidic solution corrosion, but has poor resistance to alkaline corrosion; the load softening temperature is high at 1640~1680℃; It has poor thermal shock resistance and fire resistance of 1690~1730℃.

project	index
project	BG-96A	BG-96B	BG-95	JG-94	G1-94>96
Sio₂%	≥96	≥96	≥95	≥94.5	≥94
Fe₂O₃	≤0,6	≤0,8	≤1,0	≤1,2	≤1,4
Melt index %	≤0,5	≤0,7	/	/	/
Látszólagos porozitás %	≤21	≤22	≤22	≤22	≤24
True density g/cm³	≤2.34				≤2.33
Normal temperature compressive strength MPa	≥40	≥35	≥30	≥40	≥30
0.2MPa load softening temperature℃	≥1680	≥1670	≥1670	≥1650	≥1650
Heating permanent line changes %1450℃*2h	0-0.2
Residual quartz %	≤3			≤1,5	/

Fused zirconia corundum brick

Fused zirconia corundum bricks are used to build kiln pool walls, flame space parapets, small furnace spouts, small furnace level gates, small furnace stacks, tongue gates, stb. Fused zirconia corundum bricks with 41% zirconium content are used for The corners of the masonry pool wall, the liquid flow hole, and other parts where the glass liquid has the most severe erosion on the refractory material. This material is the glass industry’s most widely used fused cast refractory.

Tétel		Ovasztott öntött AZS tégla
Index		RS-AZS33	RS-AZS36	RS-AZS41
Kémiai Összetétel%	Al2O3	≥50,00	≥49,00	≥45,00
	ZrO2	≥32,50	≥35,50	≥40,50
	SiO2	≤15.00	≤13,50	≤12,50
	Na2O+K2O	≤1,30	≤1,35	≤1,30
Térfogatsűrűség g/cm3		≥3,75	≥3,85	≥4,00
Látszólagos porozitás %		≤1,2	≤1,0	≤1,2
Hideg zúzószilárdság Mpa		≥200	≥200	≥200
Üvegfázis exudációs hőmérséklete		≥1400	≥1400	≥1410
Buborékleválasztási arány (1300 ℃ × 10 óra)		≤1,2	≤1,0	≤1,0
Üvegfolyadék korróziógátló sebessége 1500℃×36h (mm/24h)%		≤1,4	≤1,3	≤1,2
Térfogatsűrűség (g/cm3)	Közönséges öntés PT(RN RC N)	≥3,55	≥3,55	≥3,70
	Nincs zsugorodó öntvény ZWS(RR EVF EC ENC)	≥3,65	≥3,75	≥3,85
	Dönthető öntés QX(RO)	≥3,65	≥3,75	≥3,90
	Nincs zsugorodási öntvény WS( RT VF EPIC FVP DCL)	≥3,75	≥3,80	≥3,95

Magnézia tégla

The glass kiln regenerator will use 98 magnesia bricks and 96 magnesia bricks

project	MZ-95		MZ-96		MZ-97		MZ-98
project	straight bricks	Tubular brick	straight bricks	Tubular brick	straight bricks	Tubular brick	straight bricks	Tubular brick
Mgo%	≥95	≥95	≥96	≥96	≥96.7	≥96.7	≥97,2	≥97,2
Sio2 %	≤1.8	≤1.8	≤1,5	≤1,5	≤1,0	≤1,0	≤0,6	≤0,6
Ca0 %	≤2,0	≤2,0	≤1.8	≤1.8	≤1,5	≤1,5	≤1,3	≤1,3
Térfogatsűrűség g/cm3	≥2,95	≥2.93	≥2.98	≥2,95	≥3,0	≥2.98	≥3.02	≥3,0
Látszólagos porozitás %	≤17	≤18	≤16	≤17	≤15.5	≤16.5	≤15.5	≤16.5
Normal temperature compressive strength MPa	≥70	≥60	≥70	≥60	≥70	≥60	≥70	≥60
0.2MPaload softening temperature ℃	1680	1680	≥1700
Thermal shock resistance 950℃ air times	≥10

Dense zircon bricks

Dense zircon stone is manufactured using isostatic pressing/sintering technology. It has excellent properties such as high-temperature resistance, good thermal shock resistance, and resistance to glass liquid erosion. It is mainly used in the bottom and upper space of alkali-free glass and borosilicate glass tank kilns. Bricks, hook bricks, gap bricks, trough bricks, thermocouple bricks, and viewing hole bricks.

project	ZS-G	ZS-Z	ZS-65A	ZS-65B	ZS-63
Zro2 %	≥65	≥68	≥65	≥65	≥63
Sio2 %	≤33	≤30	≤33	≤33	≤35
Fe203 %	≤0,2	≤0,2	≤0,2	≤0,2	≤0,2
TiO2 %	≤1,2	≤1,2	≤1,2	≤1,2	/
Térfogatsűrűség g/cm3	≥4.3	≥4.1	≥3.7	≥3,6	≥3,55
Látszólagos porozitás %	≤1	≤11	≤17	≤19	≤20
Normal temperature compressive strength MPa	≥300	≥200	≥100	≥80	≥60
0.2MPa load softening starting temperature ℃	≥1700	≥1700	≥1680	≥1650	≥1600

Sintered zirconium corundum brick

Sintered zirconium corundum bricks have good resistance to alkali vapor and thermal shock. They are mainly used in the flame space of glass kilns, regenerator bricks, and upper grids. They can also be used in float glass kilns and daily glass kilns. Pave the bottom or forehearth with large bricks.

project	AZS-16	AZS-20	AZS-32
Zro2 %	≥16	≥20	≥32
Fe203 %	≤0,5	≤0,5	≤0,5
Térfogatsűrűség g/cm3	≥2.7	≥2.8	≥3.2
Látszólagos porozitás %	≤20	≤18	≤18
Normal temperature compressive strength MPa	≥70	≥80	≥80
0.2MPa load softening starting temperature ℃	≥1580	≥1620	≥1630

Zero expansion silica bricks for repair

The linear expansion coefficient of zero-expansion silica brick is close to 0, it has excellent thermal shock resistance, high softening temperature under load, and is safe and reliable for long-term use.

project	FS-97	FS-98	FS-99
Sio₂ %	≥97	≥98	≥98.5
Al₂0₃ %	≤0,5	≤0,3	≤0,2
Fe203 %	≤0,3	≤0,2	≤0,1
Bulk density g/cm³	≥1.75	≥1.8	≥1.85
Látszólagos porozitás %	≤22	≤20	≤18
Normal temperature compressive strength MPa	≥25	≥30	≥35
0.2MPa load softening starting temperature ℃	≥1500	≥1600	≥1650
Linear expansion rate % 1000℃	≤0,2	≤0,2	≤0,2
Thermal shock resistance 1100℃ water cooling times	≥30	≥30	≥30

Low porosity clay brick

project	DN-11	DN-14	DN-17	ZN-45	ZN-40	ZN-40
Al²0³ %	≥47	≥45	≥42	≥45	≥40	≥36
Fe₂0₃ %	≤1,2	≤1,5	≤1.8	/	/	/
Bulk density g/cm³	≥2.4	≥2.34	≥2.26	/	2.0-2.4	/
Látszólagos porozitás %	≤11	≤14	≤17	≤16	≤19（22）	≤22（24）
Normal temperature compressive strength MPa	≥80	≥65	≥50	≥60	≥40（35）	≥35（30）
0.2MPa load softening starting temperature ℃	≥1520	≥1470	≥1430	≥1430	≥1430	≥1380
Heated permanent line change % x2h	0.1~-0.21500	+0.1~-0.21400-0.2-+0.1		-0.2~+0.1	-0.3~+0.1	-0.4~+0.1