Low-porosity fire clay brick is made of low-aluminum mullite as the main raw material, which is formed by high-pressure molding and high-temperature sintering. The main mineral composition is the mullite phase, and the low-porosity clay brick has excellent high-temperature physical properties and chemical erosion resistance.

Low porosity fire clay brick physical and chemical indicators

Položka	Index
Al2Ó3  %	≥45
Fe2Ó3  %	≤1,3
Objemová hmotnost g/cm3	≥2,3
Zjevná porozita %	≤16
Pevnost v tlaku za studena MPa	≥65
Rychlost proudění % 1200℃×50h	≤0,05
Cyklus odolnosti proti tepelným šokům 1100℃ vodní chlazení	＞10

Features of low porosity clay bricks

1. Nízká pórovitost
2. Vysoká teplota měknutí při zatížení
3. High compressive strength at room temperature
4. Good volume stability at high temperatures and good wear resistance
5. Good anti-penetration and anti-corrosion properties

Comparison of low porosity clay bricks and ordinary clay bricks

Low-porosity clay bricks have good stability, no sudden change in the degree of erosion, 2-3 times longer life than ordinary clay bricks, a 2 times higher thermal conductivity and specific heat capacity than ordinary clay bricks. The heat storage capacity is 50% higher than ordinary clay bricks.

Shipping of low-porosity clay bricks

Low-porosity clay bricks can generally be shipped within 7-12 dní, except for special orders.

About Rongsheng company

Rongsheng has rich production experience in the refractory industry, especially in the production of refractory bricks and unshaped refractory materials. Vysokohlinité cihly, high purity corundum bricks, mullitové izolační cihly, andaluzitové cihly, a castable are very popular. Rongsheng has exported to more than 80 zemí. Including Russia, Jižní Afrika, Bangladesh, Egypt, France, Chile, atd.

Fire clay brick customers show

Video about Rongsheng refractory supplier

Kontaktujte nás