অ্যালুমিনিয়াম সিলিকেট Ramming উপাদান

Aluminum silicate ramming material is a kind of refractory material with high aluminum and low iron, and its main components are Al₂ও₃ and SiO₂. It is made by high-temperature sintering and high-energy grinding or ramming. It has high service temperature, strength, and density, and is mainly used in high-demand refractory structures. Rongsheng Refractory Materials also produces castables and customized ramming materials with different compositions.

Aluminum silicate ramming material details

আইটেম	Alumina-Silicon			Silicon- Carbide			Zirconium Chrome Corundum
	KSL-1	KSL-	KSL-	KSL-	KSL-	KSL-	KSL-
Al2O3 %	≥65	≥75	≥85	/	/	/	≥80
SiC %	/	/	/	≥40	≥60	≥70	/
Cr2O3 %	/	/	/	/	/	/	≥3
ZrO2 %	/	/	/	/	/	/	≥2
Bulk Density g/cm3 110℃×24h	≥2.5	≥2.7	≥2.8	≥2.4	≥2.5	≥2.6	≥2.8
Permanent Linear Change Rate % 1000℃×3h	-0.4~0	-0.5~0	-0.5~0	-0.4~0	-0.5~0	-0.6~0	-0.6~0
Cold Crushing strength MPa 1000℃×3h	≥70	≥80	≥90	≥60	≥70	≥80	≥90
Wear resistance at room temperature cm3 1000℃×3h	≤7	≤6	≤5	≤7	≤6	≤5	≤5
Thermal shock resistance 1000℃ water cooling cycle 1000℃×3h Fired	≥30	≥30	≥25	≥30	≥35	≥40	≥30
Plasticity Index %	15~55
Thermal conductivity W/(m·K) 1000℃	1.1~1.6		1.6~2.0	3~5	5~7	6~8	2~3

Production of aluminum silicate ramming mass

In manufacturing, aluminum silicate ramming materials usually need to go through multiple processes, such as screening, drying, মিশ্রণ, pounding, ইত্যাদি, to ensure uniformity and stability. Its production process and formula can be adjusted according to different needs to achieve the required fire resistance and service life.

Features of aluminum silicate ramming mass

1. High aluminum and low iron: আল₂ও₃ content is usually 55-80%, and Fe₂ও₃ content is shallow, generally not more than 3%. This can greatly increase the softening point and use temperature.
2. Dense structure: Aluminum silicate ramming material has been rammed to obtain magnificent grain structure and higher density, generally greater than 3.4g/cm³, which greatly improves its strength and slag erosion resistance.
3. High corrosion resistance: The composition of high aluminum and low iron and dense microstructure make aluminum silicate ramming material have strong resistance to acid and alkali and corrosion of various slags.
4. অনেক শক্তিশালী: the compressive strength of aluminum silicate ramming material exceeds 600MPa, which enables it to withstand greater mechanical stress and service load.
5. High working temperature: সাধারনত, it can work at a temperature above 1600-1800°C, and the maximum temperature of special varieties can reach above 2000°C.
   

1. প্র:আপনি কীভাবে আপনার গুণমান নিয়ন্ত্রণ করবেন? ক：উত্পাদন প্রক্রিয়া চলাকালীন, আমাদের কাছে একটি সম্পূর্ণ রাসায়নিক রচনা মান নিয়ন্ত্রণ ব্যবস্থা রয়েছে. উত্পাদন পরে, সমস্ত পণ্য পরীক্ষা করা হবে, এবং পণ্যগুলির সাথে একটি মানের শংসাপত্র জারি করা হবে. 2. প্র:আপনার বিতরণ সময় কি? ক：কেনা পণ্য পরিমাণের উপর নির্ভর করে, সাধারণ সময় হয় 7-12 দিন. যদি এটি একটি কাস্টমাইজড পণ্য হয়, এটা বেশি সময় লাগতে পারে. 3. প্র:আপনি কি নমুনা সরবরাহ করেন?? ক：হ্যাঁ, আমরা নমুনা সরবরাহ করতে পারি 4. প্র:আমরা কি আপনার সংস্থায় যেতে পারি?? ক：হ্যাঁ, অবশ্যই. আপনি চীনে খুব স্বাগতম এবং আমরা ক্লায়েন্ট এবং বন্ধু পেয়ে সম্মানিত হব. 5.প্র: পণ্যটি কাস্টমাইজ করা যেতে পারে? ক：আমরা কাস্টমাইজেশন সমর্থন করি, আপনি আমাদের আপনার পরিকল্পনা এবং ডিজাইন অঙ্কন প্রেরণ করতে পারেন, এবং আমরা একটি সম্পূর্ণ উত্পাদন পরিকল্পনা করব. 6. প্র:উত্সের স্থান কোথায়? ক：ঝেংজু থেকে, হেনান, চীন, 7.প্র: How to pack ক：Aluminum silicate ramming material is bagged