الفرق بين castables ومواد صدم

Castables and ramming materials are both unshaped refractory materials. تصنع المواد المصبوبة ومواد الدك من مجاميع مختلفة, مساحيق, والمجلدات بنسبة معقولة. They are both unshaped refractory materials. Although they are the same type of amorphous refractory materials, they differ greatly.

What are the differences between castables and ramming materials?

Construction methods are different

Ramming mass is constructed by ramming and hardened by heating. It is usually formed directly or after adding liquid by pounding (manual or mechanical) or vibration and hardens when the temperature is higher than room temperature.

Castables are constructed by pouring and can harden without heating. It is mainly delivered in dry form and is used after mixing with water or other liquids. Usually, vibration casting, non-vibration (self-flowing) casting, صدم, spraying, or tamping when necessary are used to form and harden without heating.

Different material classifications

Ramming materials are classified according to materials: high alumina, فخار, magnesite ramming mass, الدولوميت, zirconium, and silicon carbide-carbon refractory ramming materials.

Castables are classified by material: 1. According to porosity distribution, there are two types: dense refractory castables and insulating refractory materials with a porosity of not less than 45%; 2. According to binders, they are divided into hydraulic bonding, chemical bonding, and cohesion and combined with refractory castables.

Different applications

Castable is the most widely produced and used unshaped refractory material at present. It is mainly used to construct various heating furnace linings and other integral structures. It is used in heavy-duty furnaces and heating equipment in metallurgy, البترول, صناعة كيميائية, مواد بناء, الطاقة الكهربائية, and machinery industry. High-quality shock absorbers are widely used in metallurgy, مواد بناء, and non-ferrous metals. Smelting, المواد الكيميائية, الات, and other manufacturing industries. Products can also be used in smelting furnaces.

مادة الصدم عبارة عن مادة سائبة مصنوعة من كربيد السيليكون, الجرافيت, وأنثراسايت المكلس كهربائيا كمواد خام, يخلط مع مختلف إضافات مسحوق متناهية الصغر, and fused cement or composite resin as a binding agent. It is used to fill the gap between the furnace cooling equipment and the masonry or the filling material for the masonry leveling layer. The ramming material has good chemical stability, مقاومة التآكل, and wear resistance.